Ken,

I can't find that notebook so I'm working off memory here.

1. I usually made an 84% to 85% solids motor. Trimodal AP: 400, 200, 90 &
Under. 5% Al. They were quite reliable and reproducible.

2. For the 88% solids I added Lecithin (0.5%). Didn't use in my normal
motors.

3. Added more AP to get to 88%. Qmodal AP: 600, 400, 200, 90 & Under.

4. Had quite the "phase transition" in viscosity. After mixing for a while
it changed into a much less viscous fluid. And stayed that way through
casting.

That's all the detail I recall.

Cheers,

Brian

On Sun, Apr 30, 2023 at 1:12 AM roxanna Mason <rocketmaster.ken@xxxxxxxxx>
wrote:

That's a decent solids loading Brian, perhaps the lecithin acted as a
surfactant. Was this a single, bi or even trimodal?

Ken

On Sat, Apr 29, 2023 at 11:05 PM BrianK ABQ <cielobenazul@xxxxxxxxx>
wrote:

I briefly encountered some viscosity issues. I was trying to make some
small batch APCP with 88% solids. I recall two things.

1. A little lecithin (0.5%?) made a big difference.

2. After adding all the AP the mix really thickened. But after a bit of
mixing (20 min or so) the mix suddenly thinned and was fine to make motors
with.

Those behaviors are very finicky and formula dependent.

Cheers,

Brian